5A05 aluminum plate is Al-Mg series aluminum alloy, the strength is equivalent to 5A03, heat treatment can not be strengthened; the annealed state has high plasticity, and the plasticity is medium when semi-cold work hardening; 5A05 aluminum plate is welded by hydrogen atom welding, spot welding, gas welding, and argon arc welding. Fairly good; machinability is inferior in annealed state, machinability is fair when semi-cold hardened
 

5A05 Anodized Aluminum Plate sheet 

5A05 Anodized Aluminum Plate sheet Features:

It is a widely used aluminum alloy. This alloy has high strength, especially fatigue resistance, high plasticity and corrosion resistance, good corrosion resistance, good weldability, poor machinability, and polishing. Uses are mainly used for low-load parts that require high plasticity and good weldability, working in liquid or gaseous media, such as fuel tanks, lubricating oil pipes, various liquid containers and other small-load parts made by deep drawing

Chemical composition of 5A05 Anodized Aluminum Plate sheet

Aluminum Al: margin

Silicon Si: ≤0.50 Copper Cu: ≤0.10

Magnesium Mg: 4.8～5.5,Zinc Zn: ≤0.20

Manganese Mn: 0.30～0.6,Iron Fe: 0.000～0.500

Note: Single: ≤0.05; Total: ≤0.10,Mechanical properties:

Tensile strength σb (MPa): ≥225

Conditional yield strength σ0.2 (MPa): ≥110

Elongation δ10 (%): ≥1

Note: Longitudinal mechanical properties of pipes at room temperature

Sample size: all wall thickness